NiAl and Ni3Al sinters produced by Pulse Plasma Sintering with the SHS reaction

Abstract (EN)

The NiAl and Ni3Al matrix composites were prepared from mixtures of Ni and Al powders by using pulse plasma sintering (PPS) with participation of the self-propagation high-temperature synthesis (SHS). The sintering processes were conducted under 100 MPa for 5 min at temperatures of 1000 °C or 1100°C. The NiAl and Ni3Al sinters had above 98% of theoretical density apart from the sintering temperature. Both NiAl and Ni3Al sinters had fine grained microstructures; an average grain size was 8 µm and 4 µm, respectively. The NiAl and Ni3Al bodies sintered at 1000 °C had the hardness of 290 HV10 and 305 HV10, respectively.

Keywords (EN): PPS, NiAl, Ni3Al, SHS, Sintering

Spieki NiAl i Ni3Al wytwarzane w reakcji SHS metodą PPS

Cymerman K., Michalski A.

Abstract (PL)

Stosując metodę PPS (ang. pulse plasma sintering) z mieszaniny proszków Ni oraz Al z udziałem reakcji SHS (ang. self-propagation high-temperature synthesis) otrzymywano spieki NiAl i Ni3Al. Spiekanie prowadzono w  temperaturze 1000 °C i 1100 °C w czasie 5 min przy ciśnieniu prasowania 100 MPa. Otrzymane spieki NiAl i Ni3Al, niezależnie od temperatury spiekania, miały gęstość względną powyżej 98%. Spieki miały drobnokrystaliczną mikrostrukturę. W spiekach NiAl średnie ziarno wynosiło ok. 8 µm, natomiast w spiekach Ni3Al ok. 4 µm. Twardość spieków NiAl otrzymywanych w temperaturze 1000 °C wynosiła 290 HV10, a spieków Ni3Al - 305 HV10.

Keywords (PL): PPS, NiAl, Ni3Al, SHS, spiekanie